Synthesis and Physical and Thermodynamic Properties of Lactic Acid and Malic Acid-Based Natural Deep Eutectic Solvents
| Summary: | In this paper, four natural deep eutectic solvents (NADES) systems were prepared at specific molar ratios, La:Bet (2:1) (lactic acid/betaine), La:Hist (9:1) (lactic acid/histidine), Ma:Bet:H2O (1:2:3) (malic acid/betaine/water) and Ma:Bet:Pro:H2O (1:1:1:2) (malic acid/betaine/proline/water). Their physical and thermodynamic properties were studied, namely viscosity, electrical conductivity, and heat capacity. The viscosity and electrical conductivity were determined as a function of temperature and the correlation for the temperature dependence was obtained and discussed based on Arrhenius theory. The heat capacity for all eutectic systems was measured by differential scanning calorimetry (DSC) over a temperature range of 293.15-363.15 K. The ability of these NADES to reduce cellulose crystallinity was evaluated. Cellulose crystallinity after suspension in these NADES was studied by X-ray diffraction. Cellulose suspended in Ma/Bet/H2O (1:2:3) suffer the highest crystallinity reduction among the systems studied and was about of 20%. |
|---|---|
| Main Authors: | Castro, Vânia I. B. |
| Other Authors: | Mano, Francisca; Reis, Rui L.; Paiva, Alexandre; Duarte, Ana Rita C. |
| Subject: | Eutectics Ionic liquids Solvents DESs General Chemistry General Chemical Engineering |
| Year: | 2018 |
| Country: | Portugal |
| Document type: | article |
| Access type: | open access |
| Associated institution: | Universidade Nova de Lisboa |
| Language: | English |
| Origin: | Repositório Institucional da UNL |
| Summary: | In this paper, four natural deep eutectic solvents (NADES) systems were prepared at specific molar ratios, La:Bet (2:1) (lactic acid/betaine), La:Hist (9:1) (lactic acid/histidine), Ma:Bet:H2O (1:2:3) (malic acid/betaine/water) and Ma:Bet:Pro:H2O (1:1:1:2) (malic acid/betaine/proline/water). Their physical and thermodynamic properties were studied, namely viscosity, electrical conductivity, and heat capacity. The viscosity and electrical conductivity were determined as a function of temperature and the correlation for the temperature dependence was obtained and discussed based on Arrhenius theory. The heat capacity for all eutectic systems was measured by differential scanning calorimetry (DSC) over a temperature range of 293.15-363.15 K. The ability of these NADES to reduce cellulose crystallinity was evaluated. Cellulose crystallinity after suspension in these NADES was studied by X-ray diffraction. Cellulose suspended in Ma/Bet/H2O (1:2:3) suffer the highest crystallinity reduction among the systems studied and was about of 20%. |
|---|