In Vitro Characterization of Doped Bioglass 45S5/HAp Coatings Obtained by CoBlastTM Deposition
| Resumo: | Bone replacement is one of the major medical procedures in the oral surgery field due to the progressive ageing population and to illness or trauma in younger age groups. The use of implants without biological activity and effective osseointegration increases the chances of implant failure. This work aims to improve the interaction between implants and bone by using Bioglass 45S5 (BG)/hydroxyapatite (HAp) mixtures, including copper-, zinc-, and cerium-doped BG, as well as co-doping by the mentioned metals, as coatings produced by the CoBlastTM technique. All coatings present a uniform coverage of the Ti-6Al-4V substrate. Furthermore, in vitro testing using human osteosarcoma Saos-2 cells indicated that BG/HAp coatings have no cytotoxic effect, and the used of doping agents did not alter cell adhesion, proliferation, or alkaline phosphatase (ALP) expression when compared to undoped coating. These results demonstrate that BG/HAp by CoBlastTM can be a solution to improve implants’ osseointegration. |
|---|---|
| Autores principais: | Pádua, Ana Sofia |
| Outros Autores: | Gavinho, Sílvia Rodrigues; Vieira, Tânia; Hammami, Imen; Silva, Jorge Carvalho; Borges, João Paulo; Graça, Manuel Pedro Fernandes |
| Assunto: | Bioglass 45S5 cerium CoBlast copper hydroxyapatite implant coating zinc Surfaces and Interfaces Surfaces, Coatings and Films Materials Chemistry SDG 3 - Good Health and Well-being |
| Ano: | 2023 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Universidade Nova de Lisboa |
| Idioma: | inglês |
| Origem: | Repositório Institucional da UNL |
| Resumo: | Bone replacement is one of the major medical procedures in the oral surgery field due to the progressive ageing population and to illness or trauma in younger age groups. The use of implants without biological activity and effective osseointegration increases the chances of implant failure. This work aims to improve the interaction between implants and bone by using Bioglass 45S5 (BG)/hydroxyapatite (HAp) mixtures, including copper-, zinc-, and cerium-doped BG, as well as co-doping by the mentioned metals, as coatings produced by the CoBlastTM technique. All coatings present a uniform coverage of the Ti-6Al-4V substrate. Furthermore, in vitro testing using human osteosarcoma Saos-2 cells indicated that BG/HAp coatings have no cytotoxic effect, and the used of doping agents did not alter cell adhesion, proliferation, or alkaline phosphatase (ALP) expression when compared to undoped coating. These results demonstrate that BG/HAp by CoBlastTM can be a solution to improve implants’ osseointegration. |
|---|