Publication
Bio-based piezo- and thermoresistive photocurable sensing materials from acrylated epoxidized soybean oil
| Summary: | Bio-based photocurable polymers are increasingly in demand as environmentally friendly materials for advanced applications. Together with functional fillers, these represent a next step for the generation of functional and active smart materials, compatible with additive manufacturing technologies. Herein, acrylated epoxidized soybean oil (AESO) mixed with different amounts of reduced graphene oxide (rGO) up to 6 wt% in order to obtain UV-curable piezoresistive and thermoresistive materials, is reported. It is shown that the addition of rGO to AESO hinders the curing process, but always maintains double bond conversions higher than 50%. Composites are characterized by a good dispersion of micrometric filler clusters. Further, the thermal stabilities are close to 300 degrees C and crosslinking degrees are above 1.75 mmol cm(-3). The Young modulus of the composites decreases with the addition of the rGO fillers, in particular for the higher filler contents, and electrical conductivities up to 0.13 S m(-1) are obtained for the composites with the highest rGO content. UV-curable composites with piezoresistive and thermoresistive responses suitable for applications are thus obtained, characterized by gauge factors around 26 for deformations up to 2% and maximum thermoresistive sensitivity of S = 0.43, values similar to the values obtained for petroleum-based materials. |
|---|---|
| Main Authors: | Mendes-Felipe, Cristian |
| Other Authors: | Costa, Pedro Filipe Ribeiro; Roppolo, Ignazio; Sangermano, Marco; Lanceros-Mendez, S. |
| Subject: | bio-based resins piezoresistive devices polymer composites reduced graphene oxide UV-curing Ciências Naturais::Ciências Físicas |
| Year: | 2022 |
| Country: | Portugal |
| Document type: | article |
| Access type: | restricted access |
| Associated institution: | Universidade do Minho |
| Language: | English |
| Origin: | RepositóriUM - Universidade do Minho |
| Summary: | Bio-based photocurable polymers are increasingly in demand as environmentally friendly materials for advanced applications. Together with functional fillers, these represent a next step for the generation of functional and active smart materials, compatible with additive manufacturing technologies. Herein, acrylated epoxidized soybean oil (AESO) mixed with different amounts of reduced graphene oxide (rGO) up to 6 wt% in order to obtain UV-curable piezoresistive and thermoresistive materials, is reported. It is shown that the addition of rGO to AESO hinders the curing process, but always maintains double bond conversions higher than 50%. Composites are characterized by a good dispersion of micrometric filler clusters. Further, the thermal stabilities are close to 300 degrees C and crosslinking degrees are above 1.75 mmol cm(-3). The Young modulus of the composites decreases with the addition of the rGO fillers, in particular for the higher filler contents, and electrical conductivities up to 0.13 S m(-1) are obtained for the composites with the highest rGO content. UV-curable composites with piezoresistive and thermoresistive responses suitable for applications are thus obtained, characterized by gauge factors around 26 for deformations up to 2% and maximum thermoresistive sensitivity of S = 0.43, values similar to the values obtained for petroleum-based materials. |
|---|