Enhanced proton conductivity of Nafion-azolebisphosphonate membranes for PEM fuel cells
| Resumo: | ABSTRACT: Fuel cells are among the cleaner alternatives of sustainable energy technologies, where their proton exchange membranes continue to be a key component with many challenges and opportunities ahead. In this study, different indazole- and benzotriazolebisphosphonic acids were prepared and incorporated into new Nafion-doped membranes up to a 5 wt% loading. The new membranes were characterised, and their proton conductivities were evaluated using electrochemical impedance spectroscopy. Membranes with a 1 wt% loading showed better proton conductivities than Nafion N-115 at all temperature and under relative humidity conditions studied. In these conditions, the best value was observed for the membrane doped with [hydroxy(1H-indazol-3-yl)methanediyl]bis(phosphonic acid) (BP2), with a proton conductivity of 98 mS cm(-1). Activation energy (E-a) values suggests that both Grotthuss and vehicular mechanisms are involved in the proton conduction across the membrane. |
|---|---|
| Autores principais: | Teixeira, Fatima |
| Outros Autores: | de Sá, A.I.; Teixeira, António P. S.; Rangel, C. M. |
| Assunto: | Fuel cells Polymer electrolyte membrane PEM Proton exchange membrane |
| Ano: | 2019 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Laboratório Nacional de Energia e Geologia, I.P. |
| Idioma: | inglês |
| Origem: | Repositório do LNEG |
| Resumo: | ABSTRACT: Fuel cells are among the cleaner alternatives of sustainable energy technologies, where their proton exchange membranes continue to be a key component with many challenges and opportunities ahead. In this study, different indazole- and benzotriazolebisphosphonic acids were prepared and incorporated into new Nafion-doped membranes up to a 5 wt% loading. The new membranes were characterised, and their proton conductivities were evaluated using electrochemical impedance spectroscopy. Membranes with a 1 wt% loading showed better proton conductivities than Nafion N-115 at all temperature and under relative humidity conditions studied. In these conditions, the best value was observed for the membrane doped with [hydroxy(1H-indazol-3-yl)methanediyl]bis(phosphonic acid) (BP2), with a proton conductivity of 98 mS cm(-1). Activation energy (E-a) values suggests that both Grotthuss and vehicular mechanisms are involved in the proton conduction across the membrane. |
|---|