Publicação
Innovative improvement of sintered ceramic electrolytes by salt infiltration
| Resumo: | Previously sintered (1500 °C, 4 h) dense pellets of Ce0.9Gd0.1O1.95 (GDC) were covered and heat treated with eutectic mixtures of Na2CO3 and Li2CO3 (NLC), and their electrical performance was assessed against pure GDC and chemically synthesized GDC + NLC. Microstructural analysis of NLC impregnated samples confirmed slight migration of the molten phase to the interior of the GDC pellets via grain boundaries, resulting in a significant improvement of the grain boundary conductivity, increasing with duration of heat treatment (0.5–2 h) and temperature (600–800 °C range). The observed total conductivity exceeded in almost 20% the corresponding values obtained for standard GDC samples. Cells tested before and after direct current polarization (0.5 V, 500 °C) showed the same electrical performance, discarding the possibility of parallel contributions of salt ions to the total conductivity. Grain boundary engineering using salt infiltration is an effective tool to improve the electrical performance of ceramic electrolytes. |
|---|---|
| Autores principais: | Grilo, João P.F. |
| Outros Autores: | Macedo, Daniel A.; Nascimento, Rubens M.; Marques, Fernando M.B. |
| Assunto: | Gd-doped ceria Molten carbonates Grain boundary Impedance spectroscopy |
| Ano: | 2021 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Universidade de Aveiro |
| Idioma: | inglês |
| Origem: | RIA - Repositório Institucional da Universidade de Aveiro |
| Resumo: | Previously sintered (1500 °C, 4 h) dense pellets of Ce0.9Gd0.1O1.95 (GDC) were covered and heat treated with eutectic mixtures of Na2CO3 and Li2CO3 (NLC), and their electrical performance was assessed against pure GDC and chemically synthesized GDC + NLC. Microstructural analysis of NLC impregnated samples confirmed slight migration of the molten phase to the interior of the GDC pellets via grain boundaries, resulting in a significant improvement of the grain boundary conductivity, increasing with duration of heat treatment (0.5–2 h) and temperature (600–800 °C range). The observed total conductivity exceeded in almost 20% the corresponding values obtained for standard GDC samples. Cells tested before and after direct current polarization (0.5 V, 500 °C) showed the same electrical performance, discarding the possibility of parallel contributions of salt ions to the total conductivity. Grain boundary engineering using salt infiltration is an effective tool to improve the electrical performance of ceramic electrolytes. |
|---|