Boron Doped Ultrananocrystalline Diamond Films on Porous Silicon: Morphological, Structural and Electrochemical Characterizations
| Summary: | Boron doped ultrananocrystalline diamond (BDUND) films were grown and characterized on porous silicon (PS) substrates. PS samples were prepared from n-type monocrystalline silicon wafers (100) with 1-20 Ω.cm of resistivity, by electrochemical etching, using HF-acetonitrile solution as electrolyte. BDUND films were grown by Hot Filament Chemical Vapor Deposition using CH4, H2 and Ar. The doping process consisted of an additional hydrogen line, passing through a bubbler containing B2O3 dissolved in methanol, with boron/carbon ratio of 20000 ppm in solution. Raman spectroscopy and X-Ray diffraction were used to evaluate the quality of the films. Scanning electron microscopy was used for morphological characterization, and confirmed that the films covered the pores without filling them. Electrochemical response and capacitance behavior of the electrodes were explored, by cyclic voltammetry. Samples presented high capacitance, confirming that BDUND/PS electrodes are promising for application as electrochemical capacitors. |
|---|---|
| Main Authors: | Silva,Lilian Mieko da |
| Other Authors: | Santos,Marta dos; Baldan,Maurício Ribeiro; Beloto,Antonio Fernando; Ferreira,Neidenêi Gomes |
| Subject: | boron doped ultrananocrystalline diamond films porous silicon electrochemical application capacitance |
| Year: | 2015 |
| Country: | Brazil |
| Document type: | article |
| Access type: | open access |
| Associated institution: | IBICT |
| Language: | English |
| Origin: | Oasisbr |
| Summary: | Boron doped ultrananocrystalline diamond (BDUND) films were grown and characterized on porous silicon (PS) substrates. PS samples were prepared from n-type monocrystalline silicon wafers (100) with 1-20 Ω.cm of resistivity, by electrochemical etching, using HF-acetonitrile solution as electrolyte. BDUND films were grown by Hot Filament Chemical Vapor Deposition using CH4, H2 and Ar. The doping process consisted of an additional hydrogen line, passing through a bubbler containing B2O3 dissolved in methanol, with boron/carbon ratio of 20000 ppm in solution. Raman spectroscopy and X-Ray diffraction were used to evaluate the quality of the films. Scanning electron microscopy was used for morphological characterization, and confirmed that the films covered the pores without filling them. Electrochemical response and capacitance behavior of the electrodes were explored, by cyclic voltammetry. Samples presented high capacitance, confirming that BDUND/PS electrodes are promising for application as electrochemical capacitors. |
|---|