Effects of the atmosphere and substrate on the crystallization of PLZT thin films
| Resumo: | Lead lanthanum zirconate titanate [PLZT (9/65/35)] thin films were prepared by dip-coating on Si (100) or Si/Ti/Pt (100) substrates using a polymeric precursor solution and annealed at 650 °C for 3 h. Perovskite phase formation of the PLZT thin films and microstructure were analysed using XRD and SEM. Effects of Si (100), Si/Ti/Pt (100) substrates and atmosphere on crystallization of PLZT thin films were studied. Films deposited on platinum coated silicon (100) show a heterogeneous surface with presence of bubbles. Otherwise, the PLZT (9/65/35) thin films deposited on silicon (100) substrate shows a more uniform surface after annealing in oxygen atmosphere. |
|---|---|
| Autores principais: | Simões, A.z. |
| Outros Autores: | Gonzalez, A.h.m.; Zaghete, M.a.; Varela, J.a.; Stojanovic, B.d. |
| Assunto: | PLZT Pechini method dip-coating crystallization |
| Ano: | 2021 |
| País: | Brasil |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | IBICT |
| Idioma: | inglês |
| Origem: | Oasisbr |
| Resumo: | Lead lanthanum zirconate titanate [PLZT (9/65/35)] thin films were prepared by dip-coating on Si (100) or Si/Ti/Pt (100) substrates using a polymeric precursor solution and annealed at 650 °C for 3 h. Perovskite phase formation of the PLZT thin films and microstructure were analysed using XRD and SEM. Effects of Si (100), Si/Ti/Pt (100) substrates and atmosphere on crystallization of PLZT thin films were studied. Films deposited on platinum coated silicon (100) show a heterogeneous surface with presence of bubbles. Otherwise, the PLZT (9/65/35) thin films deposited on silicon (100) substrate shows a more uniform surface after annealing in oxygen atmosphere. |
|---|