Fabrication of fish gelatin microfibrous mats by solution blow spinning
| Resumo: | In this work microfiber mats of Nile tilapia (Oreochromis niloticus) gelatin were successfully fabricated by using Solution Blow Spinning technique. The concentration and viscosity of fish gelatin solution, in acid acetic/water (80% v/v), were correleted to the morphology and diameter of the gelatin microfibers. It was found that increased solution viscosity leads to increase of fibers diameters from approximately 280 nm at viscosity ~ 0.085 Pa.s. to approximately 1195 nm at viscosity ~ 1.877 Pa.s. The TG thermograms showed similar thermal profiles for all fibrous mat gelatins with thermal stability at temperatures below 180°C. The DSC curve showed two endothermic peaks being the second one, in the range of 100-130°C, strongly influenced by the microfiber diameters. It shifts to higher temperature increasing the microfiber diameter. This behavior was associated to the diffusion of water in the microfibers. Combined DSC/TG results showed a significant influence of the microfiber diameter on the water absorption and desorption process. |
|---|---|
| Autores principais: | Vilches, José Luiz |
| Outros Autores: | De Souza Filho, Men De Sá Moreira; De Freitas Rosa, Morsyleide; Sanches, Alex Otávio; Malmonge, José Antonio |
| Assunto: | Fish gelatin Gelatin microfiber Nile tilapia Solution blow spinning |
| Ano: | 2020 |
| País: | Brasil |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | IBICT |
| Idioma: | inglês |
| Origem: | Oasisbr |
| Resumo: | In this work microfiber mats of Nile tilapia (Oreochromis niloticus) gelatin were successfully fabricated by using Solution Blow Spinning technique. The concentration and viscosity of fish gelatin solution, in acid acetic/water (80% v/v), were correleted to the morphology and diameter of the gelatin microfibers. It was found that increased solution viscosity leads to increase of fibers diameters from approximately 280 nm at viscosity ~ 0.085 Pa.s. to approximately 1195 nm at viscosity ~ 1.877 Pa.s. The TG thermograms showed similar thermal profiles for all fibrous mat gelatins with thermal stability at temperatures below 180°C. The DSC curve showed two endothermic peaks being the second one, in the range of 100-130°C, strongly influenced by the microfiber diameters. It shifts to higher temperature increasing the microfiber diameter. This behavior was associated to the diffusion of water in the microfibers. Combined DSC/TG results showed a significant influence of the microfiber diameter on the water absorption and desorption process. |
|---|
Atividades financiadas
Não foram encontrados projetos financiados.