Positron Annihilation Spectroscopy Study on Annealing Effect of CuO Nanoparticles
| Summary: | The microstructure and defects of CuO nanoparticles under isochronal annealing were investigated by positron annihilation spectroscopy (PAS), X-ray diffraction (XRD) and scanning electron microscope (SEM). XRD and SEM results indicated that the average grain sizes of CuO nanoparticles grew slowly below 800 °C, and then increased rapidly with the annealing temperature from 800 to 1000 °C. Positron lifetime analysis exhibited that positrons were mainly annihilated in mono-vacancies (VCu , VO) and vacancy clusters when annealing from 200 to 800 °C. Furthermore,W-S plot of Doppler broadening spectra at different annealing temperatures found that the (W,S) points distributed on two different defect species, which suggested that V Cu − − V O + complexes were produced when the grains grew to bigger size after annealing above 800 °C, and positrons might annihilate at these complexes. |
|---|---|
| Main Authors: | Shi,Jianjian |
| Other Authors: | Wang,Jiaheng; Yang,Wei; Zhu,Zhejie; Wu,Yichu |
| Subject: | positron annihilation defect nanoparticle CuO |
| Year: | 2016 |
| Country: | Brazil |
| Document type: | article |
| Access type: | open access |
| Associated institution: | IBICT |
| Language: | English |
| Origin: | Oasisbr |
| Summary: | The microstructure and defects of CuO nanoparticles under isochronal annealing were investigated by positron annihilation spectroscopy (PAS), X-ray diffraction (XRD) and scanning electron microscope (SEM). XRD and SEM results indicated that the average grain sizes of CuO nanoparticles grew slowly below 800 °C, and then increased rapidly with the annealing temperature from 800 to 1000 °C. Positron lifetime analysis exhibited that positrons were mainly annihilated in mono-vacancies (VCu , VO) and vacancy clusters when annealing from 200 to 800 °C. Furthermore,W-S plot of Doppler broadening spectra at different annealing temperatures found that the (W,S) points distributed on two different defect species, which suggested that V Cu − − V O + complexes were produced when the grains grew to bigger size after annealing above 800 °C, and positrons might annihilate at these complexes. |
|---|
Funded activities
No funded projects found.