Chloroaluminium phthalocyanine polymeric nanoparticles as photosensitisers : photophysical and physicochemical characterisation, release and phototoxicity in vitro.
| Resumo: | Nanoparticles of poly(D,L-lactide-co-glycolide), poly(D,L-lactide) and polyethylene glycol-blockpoly (D,L-lactide) were developed to encapsulate chloroaluminium phthalocyanine (AlClPc), a new hydrophobic photosensitiser used in photodynamic therapy (PDT). The mean nanoparticle size varied from 115 to 274 nm, and the encapsulation efficiency ranged from 57% to 96% due to drug precipitation induced by different types of polymer. All nanoparticle formulations presented negative zeta potential values (–37 mV to –59 mV), explaining their colloidal stability. The characteristic photophysical parameters were analysed: the absorption spectrum profile, fluorescence quantum yield and transient absorbance decay, with similar values for free and nanoparticles of AlClPc. The time-resolved spectroscopy measurements for AlClPc triplet excited state lifetimes indicate that encapsulation in nanocapsules increases triplet lifetime, which is advantageous for PDT efficiency. A sustained release profile over 168 h was obtained using external sink method. An in vitro phototoxic effect higher than 80% was observed in human fibroblasts at low laser light doses (3 J/cm2) with 10 lM of AlClPc. The AlClPc loaded within polymeric nanocapsules presented suitable physical stability, improved photophysical properties, sustained released profile and suitable activity in vitro to be considered a promising formulation for PDT. |
|---|---|
| Autores principais: | Paula, Carina Silva de |
| Outros Autores: | Tedesco, Antônio Cláudio; Lucas Primo, Fernando; Vilela, José Mário Carneiro; Andrade, Margareth Spangler; Mosqueira, Vanessa Carla Furtado |
| Assunto: | Photodynamic therapy Polymeric nanoparticles Chloroaluminium phthalocyanine Release kinetic |
| Ano: | 2014 |
| País: | Brasil |
| Tipo de documento: | artigo |
| Tipo de acesso: | unknown |
| Instituição associada: | IBICT |
| Idioma: | inglês |
| Origem: | Oasisbr |
| Resumo: | Nanoparticles of poly(D,L-lactide-co-glycolide), poly(D,L-lactide) and polyethylene glycol-blockpoly (D,L-lactide) were developed to encapsulate chloroaluminium phthalocyanine (AlClPc), a new hydrophobic photosensitiser used in photodynamic therapy (PDT). The mean nanoparticle size varied from 115 to 274 nm, and the encapsulation efficiency ranged from 57% to 96% due to drug precipitation induced by different types of polymer. All nanoparticle formulations presented negative zeta potential values (–37 mV to –59 mV), explaining their colloidal stability. The characteristic photophysical parameters were analysed: the absorption spectrum profile, fluorescence quantum yield and transient absorbance decay, with similar values for free and nanoparticles of AlClPc. The time-resolved spectroscopy measurements for AlClPc triplet excited state lifetimes indicate that encapsulation in nanocapsules increases triplet lifetime, which is advantageous for PDT efficiency. A sustained release profile over 168 h was obtained using external sink method. An in vitro phototoxic effect higher than 80% was observed in human fibroblasts at low laser light doses (3 J/cm2) with 10 lM of AlClPc. The AlClPc loaded within polymeric nanocapsules presented suitable physical stability, improved photophysical properties, sustained released profile and suitable activity in vitro to be considered a promising formulation for PDT. |
|---|
Atividades financiadas
Não foram encontrados projetos financiados.