Thermoelectric properties of barium doped calcium cobaltite obtained by simplified chemical route
| Resumo: | Abstract Calcium cobaltite (CCO) thermoelectric ceramics in Ca3Co4O9 and Ca2.95Ba0.05Co4O9 compositions were produced by a simplified chemical route developed in this study. Undoped ceramics sintered at 1193 K for 12 h presented a bulk density equivalent to 77% of the theoretical density, one of the highest values ever found for conventionally sintered undoped calcium cobaltite. The presence of barium improved densification, reaching 80% of the theoretical density. Thermoelectric properties were discussed based on X-ray diffraction patterns, scanning electron micrographs, Seebeck coefficient, electrical and thermal conductivity. Electrical characterizations presented values of about 6200 and 7000 S/m at 873 K for undoped and doped ceramics, respectively. However, all ceramics presented almost the same range of activation energy values, indicating the possibility of non-effective substitution through this methodology. The maximum global PF (power factor) was 0.10 mW.m-1.K-2 for the densest undoped sample and an overall ZT (dimensionless figure of merit) of 0.07 for the undoped ceramic at 873 K. |
|---|---|
| Autores principais: | Machado,R. A. M. |
| Outros Autores: | Gelfuso,M. V.; Thomazini,D. |
| Assunto: | thermoelectric ceramics calcium cobaltite barium |
| Ano: | 2021 |
| País: | Brasil |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | IBICT |
| Idioma: | inglês |
| Origem: | Oasisbr |
| Resumo: | Abstract Calcium cobaltite (CCO) thermoelectric ceramics in Ca3Co4O9 and Ca2.95Ba0.05Co4O9 compositions were produced by a simplified chemical route developed in this study. Undoped ceramics sintered at 1193 K for 12 h presented a bulk density equivalent to 77% of the theoretical density, one of the highest values ever found for conventionally sintered undoped calcium cobaltite. The presence of barium improved densification, reaching 80% of the theoretical density. Thermoelectric properties were discussed based on X-ray diffraction patterns, scanning electron micrographs, Seebeck coefficient, electrical and thermal conductivity. Electrical characterizations presented values of about 6200 and 7000 S/m at 873 K for undoped and doped ceramics, respectively. However, all ceramics presented almost the same range of activation energy values, indicating the possibility of non-effective substitution through this methodology. The maximum global PF (power factor) was 0.10 mW.m-1.K-2 for the densest undoped sample and an overall ZT (dimensionless figure of merit) of 0.07 for the undoped ceramic at 873 K. |
|---|
Atividades financiadas
Não foram encontrados projetos financiados.