| Resumo: | A flexible piezoelectric composite with 0-3 connectivity, made from Lead Zirconate Titanate (PZT) powder and vegetable-based polyurethane (PU), was doped with small amount of semiconductor powder. As a result a composite with 0-0-3 connectivity was obtained. The nature of absorption and steady state electrical conduction and the dielectric behaviour have been studied for this ceramic/polymer composite. The dielectric loss processes of the composite were observed to be dominated by those the polymer. Adding a semiconductor phase in the composite the electrical conductivity can be controlled and a continuous electric flux path could be created between the PZT grains. This composite may be poled at low voltage and in shorter time compared with composites without a conductive phase. |
|---|---|
| Autores principais: | Sakamoto, Walter Katsumi |
| Outros Autores: | Souza, Edmilson De; Das-gupta, Dilip K. |
| Assunto: | sensors piezoelectricity pyroelectricity composites complex permittivity discharge current |
| Ano: | 2021 |
| País: | Brasil |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | IBICT |
| Idioma: | inglês |
| Origem: | Oasisbr |
| Resumo: | A flexible piezoelectric composite with 0-3 connectivity, made from Lead Zirconate Titanate (PZT) powder and vegetable-based polyurethane (PU), was doped with small amount of semiconductor powder. As a result a composite with 0-0-3 connectivity was obtained. The nature of absorption and steady state electrical conduction and the dielectric behaviour have been studied for this ceramic/polymer composite. The dielectric loss processes of the composite were observed to be dominated by those the polymer. Adding a semiconductor phase in the composite the electrical conductivity can be controlled and a continuous electric flux path could be created between the PZT grains. This composite may be poled at low voltage and in shorter time compared with composites without a conductive phase. |
|---|