Electrochemical study about zinc electrodeposition onto GCE and HOPG substrates
| Resumo: | We carried out an electrochemical study about zinc electrodeposition onto GCE and HOPG substrates from an electrolytic plating bath containing 0.01M ZnSO4 + 1M (NH4)2SO4 at pH 7. Under our experimental conditions the predominant chemical species was the complex [ZnSO4(H2O)5]. The chronoamperometric study showed that zinc electrodeposition follows a typical 3D nucleation mechanism in both substrates. The average dG calculated for the stable nucleus formation was 6.92 x 10-21 J nuclei"1 and 1.35 x 10-20 J nuclei"1 for GCE and HOPG, respectively. The scanning electron microscopy (SEM) images showed different nucleation and growth processes on GCE and HOPG substrates at same overpotential. |
|---|---|
| Autores principais: | Granados-Ner,Madai |
| Outros Autores: | Huizar,Luis Humberto Mendoza; Rios-Reyes,Clara Hilda |
| Assunto: | zinc electrodeposition carbon |
| Ano: | 2011 |
| País: | Brasil |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | IBICT |
| Idioma: | inglês |
| Origem: | Oasisbr |
| Resumo: | We carried out an electrochemical study about zinc electrodeposition onto GCE and HOPG substrates from an electrolytic plating bath containing 0.01M ZnSO4 + 1M (NH4)2SO4 at pH 7. Under our experimental conditions the predominant chemical species was the complex [ZnSO4(H2O)5]. The chronoamperometric study showed that zinc electrodeposition follows a typical 3D nucleation mechanism in both substrates. The average dG calculated for the stable nucleus formation was 6.92 x 10-21 J nuclei"1 and 1.35 x 10-20 J nuclei"1 for GCE and HOPG, respectively. The scanning electron microscopy (SEM) images showed different nucleation and growth processes on GCE and HOPG substrates at same overpotential. |
|---|
Atividades financiadas
Não foram encontrados projetos financiados.