Silver and gold nanoparticles from tannic acid: synthesis, characterization and evaluation of antileishmanial and cytotoxic activities
| Resumo: | Abstract Gold (Au0) and silver (Ag0) nanoparticles were synthesized using tannic acid (TA) as both reducing and stabilizer. Nanoparticles formation, stability, and interaction with TA were compared to citrate-coated nanoparticles and monitored by UV-Vis, zeta potential, and transmission electron microscopy. TA coating resulted in a red-shift and broadening of bands compared to citrate-coated nanoparticles (NPs-Cit). AgNPs-TA and AuNPs-TA are negatively charged with mean surface charge of -29.4 mV and -29.6 mV, respectively. TEM images showed polydispersety of AuNPs-TA (6-42 nm) and aggregation of AgNPs-TA (12-71 nm). In vitro assays of Leishmania amazonensis promastigotes showed an increment of antileishmanial activity for AgNPs-TA in relation to AgNPs-Cit, while AuNPs-TA and AuNPs-Cit did not affect the protozoas at tested concentrations. CC50 value for AgNPs-TA suggested that TA attenuates nanosilver toxicity comparatively to its precursor (Ag+). This investigation can contribute to the development of new, green, and fast produced drugs aiming at leishmaniasis treatment. |
|---|---|
| Autores principais: | LOPES,LOURDES C.S. |
| Outros Autores: | BRITO,LUCAS M.; BEZERRA,THAYLLAN T.; GOMES,KLEYTON N.; CARVALHO,FERNANDO A. DE A.; CHAVES,MARIANA HELENA; CANTANHÊDE,WELTER |
| Assunto: | green synthesis leishmaniasis metallic nanoparticles tannic acid |
| Ano: | 2018 |
| País: | Brasil |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | IBICT |
| Idioma: | inglês |
| Origem: | Oasisbr |
| Resumo: | Abstract Gold (Au0) and silver (Ag0) nanoparticles were synthesized using tannic acid (TA) as both reducing and stabilizer. Nanoparticles formation, stability, and interaction with TA were compared to citrate-coated nanoparticles and monitored by UV-Vis, zeta potential, and transmission electron microscopy. TA coating resulted in a red-shift and broadening of bands compared to citrate-coated nanoparticles (NPs-Cit). AgNPs-TA and AuNPs-TA are negatively charged with mean surface charge of -29.4 mV and -29.6 mV, respectively. TEM images showed polydispersety of AuNPs-TA (6-42 nm) and aggregation of AgNPs-TA (12-71 nm). In vitro assays of Leishmania amazonensis promastigotes showed an increment of antileishmanial activity for AgNPs-TA in relation to AgNPs-Cit, while AuNPs-TA and AuNPs-Cit did not affect the protozoas at tested concentrations. CC50 value for AgNPs-TA suggested that TA attenuates nanosilver toxicity comparatively to its precursor (Ag+). This investigation can contribute to the development of new, green, and fast produced drugs aiming at leishmaniasis treatment. |
|---|
Atividades financiadas
Não foram encontrados projetos financiados.