Characterization and electrochemical behaviour of nanostructured calcium samarium manganite electrodes fabricated by RF-Magnetron Sputtering
| Summary: | Ca1-xSmxMnO3(0 . x . 0.4) films were successfully fabricated on Indium Tin Oxide (ITO) coated quartzglass substrates by radio frequency magnetron sputtering technique (RF- magnetron sputtering) fromcompacted nanosized powder targets, and subsequent annealing at 800.C in air, for 6 h. X-ray diffrac-tion shows a pure typical perovskite phase for x . 0.1. Scanning electron microscopy and atomic forcemicroscopy revealed that the films surface is dense, with low roughness, depending on the Sm content, even though a few cracks were observed. Crystallite size was found to decrease with the Sm content. Theelectrodes were characterized by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The oxide electrode fs capacitance was estimated using both techniques and the corresponding roughness factors evaluated. The values obtained from the two methods show a good agreement. A com-parison between the voltammetric data and those referred in the literature allowed finding out that theredox reaction occurring at the electrode surface involves the pair Mn4+/Mn3+. EIS measurements con-firm the voltammetric data and they also give additional information about the film porosity and the charge transfer resistance. This last parameter is associated with the oxidation and reduction of the pairMn3+/Mn4+and after normalized by the roughness factor shows an increase with samarium content. |
|---|---|
| Main Authors: | Barrocas, B. |
| Other Authors: | Sério, S.; Rovisco, A.; Nunes, Y.; de Sá, A.I.; Pereira, M. I. da Silva; Jorge, M. E. Melo |
| Subject: | Manganites electrodes Cyclic voltammetry Magnetron sputtering Electrochemical impedance spectroscopy Electrode roughness |
| Year: | 2014 |
| Country: | Portugal |
| Document type: | article |
| Access type: | open access |
| Associated institution: | Laboratório Nacional de Energia e Geologia, I.P. |
| Language: | English |
| Origin: | Repositório do LNEG |
| _version_ | 1877768027427045376 |
|---|---|
| author | Barrocas, B. |
| author2 | Sério, S. Rovisco, A. Nunes, Y. de Sá, A.I. Pereira, M. I. da Silva Jorge, M. E. Melo |
| author2_role | author author author author author author |
| author_facet | Barrocas, B. Sério, S. Rovisco, A. Nunes, Y. de Sá, A.I. Pereira, M. I. da Silva Jorge, M. E. Melo |
| author_role | author |
| contributor_name_str_mv | Repositório do LNEG |
| country_str | PT |
| creators_json_txt | [{\"Person.name\":\"Barrocas, B.\"},{\"Person.name\":\"Sério, S.\"},{\"Person.name\":\"Rovisco, A.\"},{\"Person.name\":\"Nunes, Y.\"},{\"Person.name\":\"de Sá, A.I.\",\"Person.identifier.cienciaID\":\"B615-CCF2-424E\",\"Person.identifier.orcid\":\"0000-0003-1267-7994\"},{\"Person.name\":\"Pereira, M. I. da Silva\"},{\"Person.name\":\"Jorge, M. E. Melo\"}] |
| datacite.contributors.contributor.contributorName.fl_str_mv | Repositório do LNEG |
| datacite.creators.creator.creatorName.fl_str_mv | Barrocas, B. Sério, S. Rovisco, A. Nunes, Y. de Sá, A.I. Pereira, M. I. da Silva Jorge, M. E. Melo |
| datacite.date.Accepted.fl_str_mv | 2014-01-01T00:00:00Z |
| datacite.date.available.fl_str_mv | 2014-10-27T16:00:06Z |
| datacite.date.embargoed.fl_str_mv | 2014-10-27T16:00:06Z |
| datacite.rights.fl_str_mv | http://purl.org/coar/access_right/c_abf2 |
| datacite.subjects.subject.fl_str_mv | Manganites electrodes Cyclic voltammetry Magnetron sputtering Electrochemical impedance spectroscopy Electrode roughness |
| datacite.titles.title.fl_str_mv | Characterization and electrochemical behaviour of nanostructured calcium samarium manganite electrodes fabricated by RF-Magnetron Sputtering |
| dc.contributor.none.fl_str_mv | Repositório do LNEG |
| dc.creator.none.fl_str_mv | Barrocas, B. Sério, S. Rovisco, A. Nunes, Y. de Sá, A.I. Pereira, M. I. da Silva Jorge, M. E. Melo |
| dc.date.Accepted.fl_str_mv | 2014-01-01T00:00:00Z |
| dc.date.available.fl_str_mv | 2014-10-27T16:00:06Z |
| dc.date.embargoed.fl_str_mv | 2014-10-27T16:00:06Z |
| dc.format.none.fl_str_mv | application/pdf |
| dc.identifier.none.fl_str_mv | http://hdl.handle.net/10400.9/2546 |
| dc.language.none.fl_str_mv | eng |
| dc.publisher.none.fl_str_mv | Elsevier |
| dc.rights.none.fl_str_mv | http://purl.org/coar/access_right/c_abf2 |
| dc.subject.none.fl_str_mv | Manganites electrodes Cyclic voltammetry Magnetron sputtering Electrochemical impedance spectroscopy Electrode roughness |
| dc.title.fl_str_mv | Characterization and electrochemical behaviour of nanostructured calcium samarium manganite electrodes fabricated by RF-Magnetron Sputtering |
| dc.type.none.fl_str_mv | http://purl.org/coar/resource_type/c_6501 |
| description | Ca1-xSmxMnO3(0 . x . 0.4) films were successfully fabricated on Indium Tin Oxide (ITO) coated quartzglass substrates by radio frequency magnetron sputtering technique (RF- magnetron sputtering) fromcompacted nanosized powder targets, and subsequent annealing at 800.C in air, for 6 h. X-ray diffrac-tion shows a pure typical perovskite phase for x . 0.1. Scanning electron microscopy and atomic forcemicroscopy revealed that the films surface is dense, with low roughness, depending on the Sm content, even though a few cracks were observed. Crystallite size was found to decrease with the Sm content. Theelectrodes were characterized by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The oxide electrode fs capacitance was estimated using both techniques and the corresponding roughness factors evaluated. The values obtained from the two methods show a good agreement. A com-parison between the voltammetric data and those referred in the literature allowed finding out that theredox reaction occurring at the electrode surface involves the pair Mn4+/Mn3+. EIS measurements con-firm the voltammetric data and they also give additional information about the film porosity and the charge transfer resistance. This last parameter is associated with the oxidation and reduction of the pairMn3+/Mn4+and after normalized by the roughness factor shows an increase with samarium content. |
| dirty | 0 |
| eu_rights_str_mv | openAccess |
| format | article |
| fulltext.url.fl_str_mv | https://repositorio.lneg.pt/bitstreams/6ea02fdc-dc11-49fc-8e87-240fa8edf520/download |
| id | rlneg_e8a0513e1cee399c527e16cfafcfb5da |
| identifier.url.fl_str_mv | http://hdl.handle.net/10400.9/2546 |
| inst_facet_str | urn:organizationAcronym:rlneg{{{_:::_}}}Laboratório Nacional de Energia e Geologia, I.P. |
| instacron_str | rlneg |
| institution | Laboratório Nacional de Energia e Geologia, I.P. |
| instname_str | Laboratório Nacional de Energia e Geologia, I.P. |
| language | eng |
| network_acronym_str | rlneg |
| network_name_str | Repositório do LNEG |
| oai_identifier_str | oai:repositorio.lneg.pt:10400.9/2546 |
| organization_str_mv | urn:organizationAcronym:rlneg |
| person_str_mv | Barrocas, B. Sério, S. Rovisco, A. Nunes, Y. de Sá, A.I. de Sá, A.I. https://www.ciencia-id.pt/B615-CCF2-424E B615-CCF2-424E http://orcid.org/0000-0003-1267-7994 0000-0003-1267-7994 Pereira, M. I. da Silva Jorge, M. E. Melo |
| publishDate | 2014 |
| publisher.none.fl_str_mv | Elsevier |
| repo_facet_str | urn:repositoryAcronym:rlneg{{{_:::_}}}Repositório do LNEG |
| reponame_str | Repositório do LNEG |
| repository_id_str | urn:repositoryAcronym:rlneg |
| service_str_mv | urn:repositoryAcronym:rlneg |
| spelling | engElsevierporCa1-xSmxMnO3(0 . x . 0.4) films were successfully fabricated on Indium Tin Oxide (ITO) coated quartzglass substrates by radio frequency magnetron sputtering technique (RF- magnetron sputtering) fromcompacted nanosized powder targets, and subsequent annealing at 800.C in air, for 6 h. X-ray diffrac-tion shows a pure typical perovskite phase for x . 0.1. Scanning electron microscopy and atomic forcemicroscopy revealed that the films surface is dense, with low roughness, depending on the Sm content, even though a few cracks were observed. Crystallite size was found to decrease with the Sm content. Theelectrodes were characterized by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The oxide electrode fs capacitance was estimated using both techniques and the corresponding roughness factors evaluated. The values obtained from the two methods show a good agreement. A com-parison between the voltammetric data and those referred in the literature allowed finding out that theredox reaction occurring at the electrode surface involves the pair Mn4+/Mn3+. EIS measurements con-firm the voltammetric data and they also give additional information about the film porosity and the charge transfer resistance. This last parameter is associated with the oxidation and reduction of the pairMn3+/Mn4+and after normalized by the roughness factor shows an increase with samarium content.application/pdfporCharacterization and electrochemical behaviour of nanostructured calcium samarium manganite electrodes fabricated by RF-Magnetron SputteringBarrocas, B.Sério, S.Rovisco, A.Nunes, Y.Personalde Sá, A.I.DSpacehttp://dspace.org/items/5d35b81a-2f1b-4051-b8bc-d1a4b0934a01DSpacehttp://dspace.org/items/5d35b81a-2f1b-4051-b8bc-d1a4b0934a01SáAnaCiência IDhttps://www.ciencia-id.ptB615-CCF2-424EORCIDhttp://orcid.org0000-0003-1267-7994Pereira, M. I. da SilvaJorge, M. E. MeloHostingInstitutionOrganizationalRepositório do LNEGe-mailmailto:repositorio@lneg.ptrepositorio@lneg.ptISSNIsPartOf0013-46862014-10-27T16:00:06Z20142014-01-01T00:00:00ZHandlehttp://hdl.handle.net/10400.9/2546http://purl.org/coar/access_right/c_abf2open accessManganites electrodesCyclic voltammetryMagnetron sputteringElectrochemical impedance spectroscopyElectrode roughness156966 bytesliteraturehttp://purl.org/coar/resource_type/c_6501journal articlehttp://purl.org/coar/access_right/c_abf2application/pdffulltexthttps://repositorio.lneg.pt/bitstreams/6ea02fdc-dc11-49fc-8e87-240fa8edf520/downloadElectrochimica Acta13799107 |
| spellingShingle | Characterization and electrochemical behaviour of nanostructured calcium samarium manganite electrodes fabricated by RF-Magnetron Sputtering Barrocas, B. Manganites electrodes Cyclic voltammetry Magnetron sputtering Electrochemical impedance spectroscopy Electrode roughness |
| status | SINGLETON |
| subject.fl_str_mv | Manganites electrodes Cyclic voltammetry Magnetron sputtering Electrochemical impedance spectroscopy Electrode roughness |
| title | Characterization and electrochemical behaviour of nanostructured calcium samarium manganite electrodes fabricated by RF-Magnetron Sputtering |
| title_full | Characterization and electrochemical behaviour of nanostructured calcium samarium manganite electrodes fabricated by RF-Magnetron Sputtering |
| title_fullStr | Characterization and electrochemical behaviour of nanostructured calcium samarium manganite electrodes fabricated by RF-Magnetron Sputtering |
| title_full_unstemmed | Characterization and electrochemical behaviour of nanostructured calcium samarium manganite electrodes fabricated by RF-Magnetron Sputtering |
| title_short | Characterization and electrochemical behaviour of nanostructured calcium samarium manganite electrodes fabricated by RF-Magnetron Sputtering |
| title_sort | Characterization and electrochemical behaviour of nanostructured calcium samarium manganite electrodes fabricated by RF-Magnetron Sputtering |
| topic | Manganites electrodes Cyclic voltammetry Magnetron sputtering Electrochemical impedance spectroscopy Electrode roughness |
| topic_facet | Manganites electrodes Cyclic voltammetry Magnetron sputtering Electrochemical impedance spectroscopy Electrode roughness |
| url | http://hdl.handle.net/10400.9/2546 |
| visible | 1 |
Funded activities
No funded projects found.