Study of thermal and mechanical properties of a biocomposite based on natural rubber and 45S5 Bioglass® particles

Ver documento

Detalhes bibliográficos
Resumo:Biocomposites based on natural rubber (NR) reinforced with 45S5 Bioglass® (BG) particles were obtained by casting/evaporation method in which NR was dissolved in chloroform and mixed with BG particles. Structural, mechanical, and thermal tests were performed on the biocomposites to evaluate the influence of BG particles on the properties of the NR matrix. Thermogravimetric tests (TG/DTG) of the biocomposites showed decomposition profiles similar to that of NR, and the main peak of the DTG curve was well defined in the temperature range 300–450 °C, characteristic of the structural degradation of NR. The TG analysis also revealed that the thermal stability of the samples increases with the increasing quantity of BG in the biocomposite. DMA tests showed higher storage modulus (E′) values for samples with larger amounts of BG; however, above the Tg, the E′ value tended to zero due to the increased mobility of the polymer chains. By analyzing tan δ, the Tg values were calculated to be −46 and −50 °C for NR and the biocomposite samples, respectively. Mechanical testing demonstrated that the addition of BG to the biocomposite improved the mechanical properties of the samples. The samples became more rigid with the increasing quantity of BG, as demonstrated by decreasing deformation and the increasing elastic modulus (Y) and breaking strength of the samples. The BG particles positively affected the mechanical and thermal properties of the biocomposite, allowing its use in biomedical applications.
Autores principais:Silva, M. J.
Outros Autores:Soares, V. O.; Dias, G. C.; Santos, R. J.; Job, A. E.; Sanches, A. O.; Malmonge, J. A.
Assunto:Biocomposite Bioglass® Mechanical analysis Natural rubber Thermal analysis
Ano:2018
País:Brasil
Tipo de documento:artigo
Tipo de acesso:acesso aberto
Instituição associada:IBICT
Idioma:inglês
Origem:Oasisbr

Registos relacionados

Atividades financiadas

Não foram encontrados projetos financiados.

Registos relacionados