Brazing of zirconia to titanium using Ag-Cu and Au-Ni filler alloys

Ver documento

Detalhes bibliográficos
Resumo:Advanced ceramic is usually joined to metal by the well-known direct brazing process, where costly active filler alloys can be considered a limitation. Brazing using active-metal-free filler alloy as insert between the joint components is an attempt to overcome it. The active metal diffusion from the titanium member through the bulk of molten filler to the ceramic was responsible to produce an active filler alloy in loco and promote reduction of the zirconium oxide to improve wetting on the ceramic surface. Unalloyed titanium was joined in a high-vacuum furnace (<3x10-5 mbar) to yttria-tetragonal zirconia polycristals (Y-TZP) and zirconia partially stabilized with magnesia (Mg-PSZ), where commercial fillers Ag-28Cu and Au-18Ni with respective thermal cycles were evaluated. Helium gas leak detection test was performed at the ceramic/metal interface at room temperature; samples from reliable vacuum tight joints were examined by microstructural analysis techniques and energy dispersive X-ray analysis at the joint cross-section. Tight joints were produced with eutectic Ag-Cu filler, revealing an intermetallic layer and a dark reaction layer near the ceramic surface; titanium diffusion was efficient for superficial chemical interactions between individual components. Brazing joints were also tested using three-point flexure testing.
Autores principais:Pimenta,Jean S.
Outros Autores:Buschinelli,Augusto J. A.; Nascimento,Rubens M. do; Martinelli,Augusto E.; Remmel,Joseph
Assunto:Brazing Zirconia Titanium Ceramic/metal joining
Ano:2013
País:Brasil
Tipo de documento:artigo
Tipo de acesso:acesso aberto
Instituição associada:IBICT
Idioma:inglês
Origem:Oasisbr

Registos relacionados

Atividades financiadas

Não foram encontrados projetos financiados.

Registos relacionados