Effect of etching and light-curing time on the shear bond strength of a resin-modified glass ionomer cement

Ver documento

Detalhes bibliográficos
Resumo:The aim of this study was to assess the influence of etching and light-curing time on the shear bond strength (SBS) and adhesive remnant index (ARI) of a resin-modified glass ionomer cement (RMGIC) upon debonding of orthodontic brackets. Sixty-eight bovine permanent incisors were obtained and embedded in acrylic resin. Edgewise metallic brackets were bonded to the teeth with Fuji Ortho LC RMGIC. The specimens were randomly assigned to 4 groups, using the following etching and light-curing times: G1: 10% polyacrylic acid and 40 s (control); G2: 37% phosphoric acid and 40 s; G3: 10% polyacrylic acid and 50 s; and G4: 37% phosphoric acid and 50 s. Shear test was performed at 0.5 mm/min and the ARI was assessed. G2 (3.6 ± 0.98 MPa) presented significantly higher (p<0.05) SBS than G1 (2.76 ± 0.86 MPa) and G4 (2.86 ± 0.68 MPa), and there was no statistically significant difference (p&gt;0.05) between G2 and G3 (2.94 ± 0.67 MPa). ARI presented prevalence of scores 2 and 3 in all groups. RMGIC SBS enhanced with 37% phosphoric acid etching and 40 s light-curing time, but this did not occur when the light-curing time was increased, regardless of the acid used. RMGIC presented prevalence of failures at the adhesive/bracket interface.
Autores principais:Maruo,Ivan Toshio
Outros Autores:Godoy-Bezerra,Juliana; Saga,Armando Yukio; Tanaka,Orlando Motohiro; Maruo,Hiroshi; Camargo,Elisa Souza
Assunto:orthodontics bonding resin-modified glass ionomer cement
Ano:2010
País:Brasil
Tipo de documento:artigo
Tipo de acesso:acesso aberto
Instituição associada:IBICT
Idioma:inglês
Origem:Oasisbr

Registos relacionados

Atividades financiadas

Não foram encontrados projetos financiados.

Registos relacionados