Effect of different surface treatments and multimode adhesive application on the Weibull characteristics, wettability, surface topography and adhesion to CAD/CAM lithium disilicate ceramic

Ver documento

Detalhes bibliográficos
Resumo:This paper aims to evaluate the effect of different surface treatments on surface topography, wettability, and shear bond strength of resin cement to glass ceramic. Methodology: For SBS test, 32 blocks (7x7x2 mm) of lithium disilicate were obtained and randomly divided into eight groups (four blocks per group) according to each surface treatment (HF 20 s, 60 s, 120 s + silanization/S or Scotch Bond Universal/ SBU) and the Monobond Etch & Prime - MEP application followed or not by SBU. On each treated surface ceramic block, up to four dual-curing resin cement cylinders were prepared and light-cured for 40s (N=120/n=15). The specimens were thermocycled (10,000 cycles, 5-55°C, 30 s) and the SBS test (50KgF, 0.5 mm/min) was performed. Furthermore, failure analysis, wettability, AFM, and SEM were carried out. SBS data (MPa) were analyzed using Student's t-test, two-way ANOVA, Tukey's test (5%) and Weibull's analysis. Results: For HF experimental groups, two-way ANOVA presented the factors “etching time” and “bonding agent” as significant (p<0.05). After silane application, the HF groups presented similar bond strength. SBU application compromised the SBS, except for 120s etching time (HF120sS: 23.39ᵃ±6.48 MPa; HF120sSBU: 18.76ᵃ±8.81MPa). For MEP groups, SBU application did not significantly affect the results (p=0.41). The MEP group presented the highest Weibull modulus (4.08A) and they were statistically different exclusively from the HF20sSBU (0.58B). Conclusion: The HF 20s, 60s, 120 s followed by silane, promoted similar resin-bond strength to ceramic and the SBU application after HF or MEP did not increase the SBS.
Autores principais:Souza, Karina Barbosa
Outros Autores:Moura, Dayanne Monielle Duarte; Silva, Sarah Emille Gomes da; Araújo, Gabriela Monteiro de; Pinto, Rafael de Almeida Spinelli; Leite, Fabíola Pessôa Pereira; Özcan, Mutlu; Souza, Rodrigo Othávio de Assunção e
Assunto:Dental Ceramics Resin Cement Shear Strength
Ano:2021
País:Brasil
Tipo de documento:artigo
Tipo de acesso:unknown
Instituição associada:IBICT
Idioma:inglês
Origem:Oasisbr

Registos relacionados

Atividades financiadas

Não foram encontrados projetos financiados.

Registos relacionados