Phosphoric acid adsorbed on silica-ceria matrix obtained by sol-gel method: studies of local structure, texture and acid property

Ver documento

Detalhes bibliográficos
Resumo:SiO2/CeO2 mixed oxide (designated as SC) with variable ceria contents, SC1 = 5.6, SC2 = 8.0 and SC3 = 13.0 wt%, prepared by the sol-gel processing method, were obtained as amorphous solids possessing specific surface areas of SC1 = 463, SC2 = 474 and SC3 = 460 m²g-1. Phosphate ions were immobilized onto the surface of these solids through Ce-O-P bonding by immersing SC into a phosphoric acid solution. Solids with the following P contents were obtained (in atom %): SCP1 = 0.60, SCP2 = 0.71 and SCP3 = 1.63. The binding energy peak P 2p3/2 at ca. 134.0 eV, observed by XPS, and the 31P MAS NMR single peak, observed at ca. -10 ppm, revealed that H2PO4- is the species present on the surface of the matrices. Using pyridine as a molecular probe, only Brønsted acid sites could be detected. The amount of these acid sites, determined by ammonia gas adsorption on the surface, reached the following values for each phosphate-treated solid: SCP1 = 0.37, SCP2 = 0.43 and SCP3 = 0.51 mmol g-1.
Autores principais:Pissetti,Fábio L.
Outros Autores:Francisco,Maria Suzana P.; Landers,Richard; Gushikem,Yoshitaka
Assunto:silica-ceria silica-ceria-phosphate sol-gel method acid sites
Ano:2007
País:Brasil
Tipo de documento:artigo
Tipo de acesso:acesso aberto
Instituição associada:IBICT
Idioma:inglês
Origem:Oasisbr

Registos relacionados

Atividades financiadas

Não foram encontrados projetos financiados.

Registos relacionados