The present experiment describes the preparation, characterization of n-butyl(pyridil)cobaloxime complex and its electrochemical property. The infrared and uv-visible absorption spectra were used to characterize the complex obtained. The infrared spectrum of the compound showed characteristics bands that indicated the formation of the Co-C chemical bond formation. The electronic absorption spectrum in acetonitrile showed transition bands attributed to p-p*, metal-to-ligand charge transfer, d-d transitions and charge transfer Co-C. The electrochemical property was investigated by the pulse differential voltammetry technique. Two oxidation processes: Co(I)/Co(II) at -423 mV and Co(II)/Co(III) at 752 mV were observed.

The present experiment describes an easy procedure for obtaining SiO2/ZrO2 by reacting ZrOCl2 with SiO2 with the following characteristics: S BET = 500 m² g-1 and an average pore diameter of 6 nm. The material obtained presented 1.3 wt% ZrO2 content corresponding to 140 mumol g-1. The average density of ZrO2 onto SiO2/ZrO2 matrix is 2.8x10-11 mol cm-2. The adsorption isotherm for Cr(VI) showed a maximum of adsorption value (200 mumol g-1) at pH 2. The adsorption can be described by the reaction: =Zr(OH)2 + 2HCrO4- + 2H+ <IMG SRC="http:/img/fbpe/qn/v25n3/9346fr1.gif">[(=Zr(OH2+)2) (HCrO4-)2]. Above the zero point of charge, i.e. pH > 5.5 due to the surface charge inversion, desorption of Cr(VI) occurs according to the reaction: [(=Zr(OH2+)2) (HCrO4-)2] + 6OH- <IMG SRC="http:/img/fbpe/qn/v25n3/9346fr1.gif">(=ZrO2)2- + 6H2O + 2CrO4(2-).