Coaxial electrospinning is a technique that allows the production of nanofibers with a core–shell structure. Such fibers present several advantages as materials for the preparation of scaffolds, namely due to the possibility of combining a core with the desired mechanical properties with a shell prepared from biocompatible materials that will establish proper interactions with the host. Herein, core-shell fibrous meshes, composed of a polycaprolactone (PCL) core and a functionalized gelatin shell, were prepared by coaxial electrospinning and then photocrosslinked under UV light aiming to be used in vascular tissue regeneration. The suitability of the meshes for the pretended biomedical application was evaluated by assessing their chemical/physical properties as well as their haemo and biocompatibility in vitro. The obtained results revealed that meshes’ shell prepared with a higher content of gelatin showed fibers with diameters presenting a unimodal distribution and a mean value of 600 nm. Moreover, those fibers with higher content of gelatin also displayed lower water contact angles, and therefore higher hydrophilicities. Such features are crucial for the good biologic performance displayed by these meshes, when in contact with blood and with Normal Human Dermal Fibroblasts cells.

Cardiovascular disease is the leading cause of morbidity and mortality among industrialized countries. Vascular grafts are often required for the surgical treatments. Considering the limitations associated with the use of autografts and with the currently available synthetic materials, a growing demand in tissue engineered vascular grafts has been registered. During the work here described, electrospinning technique was used to prepared fibrous matrices to be applied as vascular implants. For that purpose, electrospun polycaprolactone (PCL) fibrous mats were produced and afterwards coated with different hydrogel formulations based in photocrosslinkable gelatin (GelMA) and the macromers poly(ethylene glycol) acrylate (PEGA) and poly(ethylene glycol) diacrylate (PEGDA). These were further photocrosslinked under UV irradiation using Irgacure® 2959 (by BASF) as the photoinitiator. The suitability of the coated scaffolds for the intended application, was evaluated by assessing their chemical/physical properties as well as their interaction with blood and endothelial cells.

Novel photocurable and low molecular weight oligomers based on l-lactic acid with proven interest to be used as bioadhesive were successfully manufactured. Preparation of lactic acid oligomers with methacrylic end functionalizations was carried out in the absence of catalyst or solvents by self-esterification in two reaction steps: telechelic lactic acid oligomerization with OH end groups and further functionalization with methacrylic anhydride. The final adhesive composition was achieved by the addition of a reported biocompatible photoinitiator (Irgacure® 2959). Preliminary in vitro biodegradability was investigated by hydrolytic degradation in PBS (pH = 7.4) at 37 °C. The adhesion performance was evaluated using glued aminated substrates (gelatine pieces) subjected to pull-to-break test. Surface energy measured by contact angles is lower than the reported values of the skin and blood. The absence of cytoxicity was evaluated using human fibroblasts. A notable antimicrobial behaviour was observed using two bacterial models (Staphylococcus aureus and Escherichia coli). The cured material exhibited a strong thrombogenic character when placed in contact with blood, which can be predicted as a haemostatic effect for bleeding control. This novel material was subjected to an extensive characterization showing great potential for bioadhesive or other biomedical applications where biodegradable and biocompatible photocurable materials are required.

L-lactic acid was the starting material for obtaining bioahesives. Reaction with 1,4-butanediol provided a telechelic lactic acid prepolymer with hydroxyl end groups further functionalized with 2-isocyanatoethyl methacrylate. Films were produced upon UV irradiation, 2 min, after addition of Irgacure 2959. This was a solvent and catalyst free process. Thermal characterization of films confirmed stability at physiological temperature, enabling photocuring. Adhesion properties were assessed with good results. In vitro degradation tests showed moderate hydrolytic instability dependent on thickness. SEM images revealed a uniform and compact structure. Thrombosis tests confirmed the materials’ thrombogenicity while biocompatibility experiments showed fibroblast viability and antimicrobial behavior.

Electrospun polymeric meshes are known to exhibit promising properties for the regeneration of several soft tissues. Herein, electrospun polymeric meshes were prepared from blends of polycaprolactone and functionalized gelatin. The meshes were then photocrosslinked under UV light using Irgacure® 2959 as the photoinitiator, aiming to improve membranes’ stability in biological fluids. Moreover, meshes suitability to be used as vascular grafts was evaluated by characterizing their chemical/physical properties as well as their haemo and biocompatibility in vitro. The obtained results show that the blended polymeric meshes are biodegradable and those with a higher content of gelatin display a lower water contact angle. Blood compatibility studies showed that the photocrosslinked membranes are haemocompatible, i.e. they display low values of thrombogenicity and do not trigger any haemolytic effect. Also, Normal Human Dermal Fibroblasts cells were incubated in the presence of the produced membranes and they were able to adhere and proliferate, thus revealing the biocompatibility of the photocrosslinked meshes.

Healing enhancement and pain control are critical issues on wound management. So far, different wound dressings have been developed. Among them, hydrogels are the most applied. Herein, a thermoresponsive hydrogel was produced using chitosan (deacetylation degree 95%) and agarose. Hydrogel bactericidal activity, biocompatibility, morphology, porosity and wettability were characterized by confocal microscopy, MTS assay and SEM. The performance of the hydrogel in the wound healing process was evaluated through in vivo assays, during 21 days. The attained results revealed that hydrogel has a pore size (90–400 μm) compatible with cellular internalization and proliferation. A bactericidal activity was observed for hydrogels containing more than 188 μg/mL of chitosan. The improved healing and the lack of a reactive or a granulomatous inflammatory reaction in skin lesions treated with hydrogel demonstrate its suitability to be used in a near future as a wound dressing.

The preparation of photocrosslinkable bioadhesives synthesized from oligomers of lactic acid and polycaprolactone (PCL), both functionalized with 2-isocyanoethyl acrylate (AOI), were studied. The obtained modified macromers of LA-AOI (mLA) and PCL-AOI (mCL) were chemically characterized by 1H NMR and used to formulate polymeric blends with different mass proportions, 1:1, 1:2 and 2:1, respectively. Subsequently, the produced blends were crosslinked, considering two UV irradiation times: 30 and 120 s. After their production, the thermal and mechanical properties of bioadhesives were assessed, where upon the rheology, gel content, hydrolytic degradation and dynamic contact angles were determined. Furthermore, the cytotoxic profile of bioadhesives was evaluated in contact with human dermal fibroblasts cells, whereas their antibacterial effect was studied monitoring Escherichia coli and S. aureus growth. Overall, flexible and resistant films were obtained, presenting promising features to be used as surgical bioadhesives.

Novel biodegradable and low cytotoxic poly(ester amide)s (PEAs) based on α-amino acids and (L)-lactic acid (L-LA) oligomers were successfully synthesized by interfacial polymerization. The chemical structure of the new polymers was confirmed by spectroscopic analyses. Further characterization suggests that the α-amino acid plays a critical role on the final properties of the PEA. L-phenylalanine provides PEAs with higher glass transition temperature, whereas glycine enhances the crystallinity. The hydrolytic degradation in PBS (pH = 7.4) at 37 °C also depends on the α-amino acid, being faster for glycine-based PEAs. The cytotoxic profiles using fibroblast human cells indicate that the PEAs did not elicit an acute cytotoxic effect. The strategy presented in this work opens the possibility of synthesizing biodegradable PEAs with low citotoxicity by an easy and fast method. It is worth to mention also that the properties of these materials can be fine-tuned only by changing the α-amino acid.

A large group of low molecular weight natural compounds that exhibit antimicrobial activity has been isolated from animals and plants during the past two decades. Among them, peptides are the most widespread resulting in a new generation of antimicrobial agents with higher specific activity. In the present study we have developed a new strategy to obtain antimicrobial wound-dressings based on the incorporation of antimicrobial peptides into polyelectrolyte multilayer films built by the alternate deposition of polycation (chitosan) and polyanion (alginic acid sodium salt) over cotton gauzes. Energy dispersive X ray microanalysis technique was used to determine if antimicrobial peptides penetrated within the films. FTIR analysis was performed to assess the chemical linkages, and antimicrobial assays were performed with two strains: Staphylococcus aureus (Gram-positive bacterium) and Klebsiella pneumonia (Gram-negative bacterium). Results showed that all antimicrobial peptides used in this work have provided a higher antimicrobial effect (in the range of 4 log-6 log reduction) for both microorganisms, in comparison with the controls, and are non-cytotoxic to normal human dermal fibroblasts at the concentrations tested.

Recently, bone tissue engineering emerged as a viable therapeutic alternative, comprising bone implants and new personalized scaffolds to be used in bone replacement and regeneration. In this study, biocompatible scaffolds were produced by freeze-drying, using different formulations (chitosan, chitosan/gelatin, chitosan/β-TCP and chitosan/gelatin/β-TCP) to be used as temporary templates during bone tissue regeneration. Sample characterization was performed through attenuated total reflectance-Fourier transform infrared spectroscopy, X-ray diffraction and energy dispersive spectroscopy analysis. Mechanical characterization and porosity analysis were performed through uniaxial compression test and liquid displacement method, respectively. In vitro studies were also done to evaluate the biomineralization activity and the cytotoxic profile of the scaffolds. Scanning electron and confocal microscopy analysis were used to study cell adhesion and proliferation at the scaffold surface and within their structure. Moreover, the antibacterial activity of the scaffolds was also evaluated through the agar diffusion method. Overall, the results obtained revealed that the produced scaffolds are bioactive and biocompatible, allow cell internalization and show antimicrobial activity against Staphylococcus aureus. Such, make these 3D structures as potential candidates for being used on the bone tissue regeneration, since they promote cell adhesion and proliferation and also prevent biofilm development at their surfaces, which is usually the main cause of implant failure.