This paper describes an experimental research that aimed to evaluate the mechanical performance of concrete made with recycled ceramic coarse aggregates from industrial brick waste. Concretes incorporated natural fine aggregates (NFA), natural coarse aggregates (NCA) and the ceramic recycled coarse aggregates (RCA). The aggregates were characterized by particle size distribution, flakiness index, shape index, particle density, water absorption, loose bulk density, voids, crush resistance and resistance to fragmentation. Once the aggregates were studied, concretes were produced with RCA replacing NCA in absolute volume percentages of 0%, 10%, 30%, 50% and 75%. All the concretes were produced with the same workability and aggregate size gradation. In the hardened state, concretes were evaluated by the compressive strength, flexural strength, tensile splitting strength and density. The results showed the feasibility of partial replacement of NCA by RCA, despite the mechanical performance of concrete decreases with increasing replacement of NCA by RCA.

Concrete compressive strength of standard samples curing under standard conditions are of outmost importance for quality control of concrete as it is produced. However, those values can only be accepted as indicating the “potential strength” of concrete and may differ from the actual in-situ concrete compressive strength. The knowledge, as close as possible, of the in-situ concrete compressive strength is, in some situations, necessary in order to estimate, for instance: the time when precast concrete members can be moved and transported, the time of prestress, removal of moulds or propping, etc. Non-destructive tests (NDT) have been increasingly used in the last decades for this purpose, i. e., the assessment of in-situ quality and integrity of concrete elements, especially for estimation of the in-situ concrete compressive strength. The use of NDT methods on normal and high strength concrete elements will be evaluated on this paper qualitatively, taking as reference five different test methods, which imply the measurement of other five different properties. Such properties include the measurement of the surface hardness, ultra-sonic pulse velocity, penetration resistance, pull-out force and direct tensile strength (pull-off test).

The existence of a relationship between the compressive strength of a given concrete and its resistance to penetration by a steel probe fired into the concrete is well known; the depth of penetration will be inversely proportional to the compressive strength. A test apparatus, designed for this purpose, using a special probe and standardised powder charge, was developed in the USA during the 1960s’ and is known as Windsor Probe Test and covered by the ASTM Standards (ASTM-C803-90). In Europe, similar standards are the British Standards (BS 1881: Part 207: 1992). The aim of this work is to perform studies concerning to a new apparatus application in comparison with the WPT System, which was called Alternative Firing Apparatus (AFA). Five different mix proportions were produced in order to obtain five sets of specimens with five different classes of compressive strength. The tests with the two described systems were performed at 28 days age for each set of specimens. The obtained results show that the Alternative Firing Apparatus could be a suitable mean for the assessment of in-place strength. The main physical limitation of penetration resistance tests is the surface damage and the danger of splitting of members, which limits the zones of testing. However, it was found that the Alternative Firing Apparatus causes less damage than WPT System. Consequently, minor distances between probes are possible.

Estatísticas publicadas pelo Instituto de Segurança Pública têm impulsionado a busca crescente por métodos de construção que ampliem a sensação de segurança, marcando os últimos anos com um notável aumento nos investimentos em sistemas de blindagem. O concreto, por sua vez, se revela como um importante para o desenvolvimento de produtos com esse propósito, e apresenta resultados promissores quando submetido a impactos balísticos. Este estudo apresenta o desempenho de amostras de concreto com uma resistência média à compressão de 40 MPa, que foram submetidas a impactos balísticos causados por projéteis de calibres nominais de 0.40" e 5.56 mm. Para a realização do experimento, foram fabricados corpos de prova de concreto cilindricos e prismáticos. Os cilindricos passaram por ensaios de compressão usando uma prensa Solotest, enquanto os prismaticos foram submetidos ao ensaio de impactos balísticos disparados a uma distância de quinze metros. Os ensaios revelaram a ocorrência de danos locais, como a formação de crateras e túneis, sem que fossem identificados danos globais Esses resultados destacam a capacidade do concreto, com uma resistência à compressão de 40 MPa, de resistir a impactos provocados por projéteis de calibres 5.56 mm e 0.40", mesmo sem a aplicação de reforços adicionais.

As estruturas de concreto pré-moldado apresentam facilidade de execução e de controle de qualidade de seus elementos. Porém, as ligações entre os elementos são o principal problema. A máxima economia do projeto ocorre quando os elementos de ligação possuem desempenho adequado e fácil montagem. Uma forma de ligação entre pilar e viga é através de consolo de concreto. Consolos são elementos estruturais que se projetam de pilares para servir de apoio para outras partes da estrutura. O presente trabalho apresenta uma revisão bibliográfica acerca dos principais conceitos para a pesquisa e engloba um programa experimental no qual foram ensaiados seis modelos em escala reduzida com consolos curtos de mesma dimensão. Quatro modelos apresentaram taxas de armadura iguais, variando o método de ancoragem do tirante e a forma de concretagem do consolo: monolíticos ou em etapa posterior à execução do pilar. Dois modelos possuem taxa de armadura do pilar superior e taxa de armadura de costura inferior aos dos modelos mencionados anteriormente. Estes dois modelos foram monolíticos e a forma de ancoragem do tirante foi variada. Dessa forma, foi possível avaliar o comportamento e a segurança de consolos curtos monolíticos e concretados em etapa posterior à execução do pilar com estribos na região de ancoragem. Foram avaliadas a influência de estribos na região de ancoragem, a contribuição da armadura de costura na resistência dos consolos e a influência da variação das taxas de armadura do pilar e do consolo no modo de ruptura. Todos os modelos comportaram-se de forma dúctil e apresentaram cargas últimas maiores que o previsto por normas. Os modelos de cálculo teóricos forneceram valores mais próximos aos observados experimentalmente devido ao fato deles considerarem a contribuição da armadura de costura no cálculo da resistência. Constatou-se que os estribos na região de ancoragem contribuíram para aumentar a rigidez do consolo e que o modo de ruptura do modelo depende do trabalho conjunto entre a armadura do consolo e do pilar.